200℃ Heat Shrink Viton Tubing is suitable to many applications requiring high resistance to corrosive fluids, fuels, lubricants, acids and solvents at elevated temperature.
Back to list >> 
200℃ Heat Shrink Viton Tubing is made from modified fluoroelastomer (Viton), with superior impact, abrasion and cut
through resistant, it is suitable to many applications requiring high resistance to corrosive fluids, fuels, lubricants, acids and
solvents at elevated temperature.
Features
>Approval: UL, VW-1,
>Meet: SAE-AMS-DTL-23053/13
>Very flexible
>Excellent resistance of chemicals
>Operating temperature -55℃ to +200℃
>Minimum fully recovery temperature: 175℃
>Standard color: Black
| Property | Test Method | Typical Data |
| Operating temperature | IEC 216 | -55℃ to +200℃ |
| Tensile strength | ASTM D 2671 | 8.5MPa |
| Elongation at break | ASTM D 2671 | 250% |
| Elongation at break after aging | 250℃/168hrs. | 200% |
| Heat shock | 300℃/4hrs. | No cracking or dropping |
| Flexibility | ASTM D 412 | 13.8MPa |
| Flammability | ASTM D 2671 | Self-extinguish in 15sec. |
| Volume resistance | ASTM D 876 | 109Ω.cm |
| Dielectric strength | ASTM D 2671 | 7.9kV/mm |
| Copper corrosion | SAE-AMS-DTL-23053/13 (175℃/16hrs.) | No corrosion |
| Normal size | As supplied(mm) | After recovered (mm) | Tube shape | Standard length(m/spool) | ||
| (inch) | (mm) | Inside diameter (Min.) | Inside diameter (Max.) | Wall thickness (Nom.) | ||
1/8 | 3.2 | 3.2 | 1.6 | 0.76±0.20 | O | 50 |
3/16 | 4.8 | 4.8 | 2.4 | 0.89±0.20 | O | 50 |
1/4 | 6.4 | 6.4 | 3.2 | 0.89±0.20 | O | 50 |
3/8 | 9.5 | 9.5 | 4.8 | 0.89±0.20 | – | 50 |
1/2 | 12.7 | 12.7 | 6.4 | 0.89±0.20 | – | 30 |
3/4 | 19.1 | 19.1 | 9.5 | 1.07±0.30 | – | 30 |
1 | 25.4 | 25.4 | 12.7 | 1.25±0.30 | – | 30 |
1-1/2 | 38.1 | 38.1 | 19.1 | 1.40±0.30 | – | 15 |
2 | 50.8 | 50.8 | 25.4 | 1.65±0.30 | – | 10 |
Remarks:
1. (Viton®) is a registered trademark of E.L Du Pont de Nemours and Co.Inc
2. Tube shape: “O” : Round or Oval, “—”: Flat