Heat Shrinkable Cable Repair Sleeve (HSRS-N) is made of a cross-linked, heat-shrinkable, thermally stabilized polyolefin, which is coated with a hot-melt adhesive .
Back to list >> 
Heat Shrinkable Cable Repair Sleeve (HSRS-N) is made of a cross-linked, heat-shrinkable, thermally stabilized polyolefin, which is coated with a hot-melt adhesive, it will bond at the temperatures attained during the shrinking operation. The HSRS-N has an aluminum canister providing mechanical protection of joint. Flexible crowns at the ends provide a smooth transition from the joint to the cable.
Property | Test Method | Standard Value |
Tensile strength | ASTM-D-638 | ≥13MPa |
Elongation at break | ASTM -D- 638 | ≥300% |
Tensile strength after aging | ASTM-D-2671/120℃,168hrs | ≥11MPa |
Elongation at break after aging | ASTM-D-2671/120℃,168hrs | ≥210% |
Volume resistance | ASTM-D-2303 | ≥1×1014Ω·cm |
Dielectric strength | IEC 243 | ≥20kV/mm |
Longitudinal shrinkage | - | ≤ 10% |
Eccentricity | ASTM-D-267 | ≤30% |
Water absorption | ISO 62 | ≤0.1% |
Item | Width（mm) | Wall thickness （mm) | ||
Before shrink（≥） | After shrink（≤） | Before shrink | After shrink | |
Ф 30 | 120 | 37 | 1.1±0.2 | 3.8±0.2 |
Ф 40 | 130 | 37 | 1.0±0.2 | 3.8±0.2 |
Ф 50 | 160 | 52 | 1.1±0.2 | 3.8±0.2 |
Ф 65 | 205 | 74 | 1.1±0.2 | 3.8±0.2 |
Ф 85 | 270 | 85 | 1.0±0.2 | 3.8±0.2 |
Ф 100 | 320 | 85 | 1.0±0.2 | 3.8±0.2 |
Ф 120 | 380 | 125 | 1.3±0.2 | 3.8±0.2 |
Ф 150 | 475 | 155 | 1.3±0.2 | 3.8±0.2 |
Ф 160 | 505 | 155 | 1.2±0.2 | 3.8±0.2 |
Ф 195 | 590 | 218 | 1.0±0.2 | 2.3±0.2 |
Ф 240 | 735 | 280 | 1.0±0.2 | 2.3±0.2 |
Ф 290 | 900 | 365 | 1.0±0.2 | 2.3±0.2 |
*Alternative for Raychem CRSM,3M HDCW, CANUSA CRDW